Product Details

Iron alloy powder used for Centrifugal casting on cylinder ID surface.
Global Fusion Iron alloy powder specifications:

Powder

HRC

Chemical Composition

Coating/Overlaying Process  

Mesh Size

C

Cr

Si

Fe

Mo

Ni

Mn

B

Others

Fe101

62

3.3

2

1

Bal

 

5

1

1.4

 

Centrifugal casting on cylinder ID surface

20/300

Fe102

62

2.7

2.8

1

Bal

 

5.5

1

1.9

 

Centrifugal casting on cylinder ID surface

20/300

Fe103

62

1.5

4.5

1

Bal

 

7

1

2.9

 

Centrifugal casting on cylinder ID surface

20/300

Fe103-5

63

1.5

6

2

Bal

 

8

1.5

3

 

Centrifugal casting on cylinder ID surface

10/300

Fe103-5A

62

2

10

2

Bal

1.1

7.5

1.2

3.6

 

Centrifugal casting on cylinder ID surface

10/200

Fe103WM

61

1.5

7.2

2.3

Bal

2.5

10

0.6

3

W:1.20

Centrifugal casting on cylinder ID surface

10/200

Fe104

60

1.7

4.5

1.5

Bal

 

11

0.8

3

 

Centrifugal casting on cylinder ID surface

20/300

Fe105

62

1.5

5.5

1.3

Bal

1.5

12

1

2.8

W:4.50

Centrifugal casting on cylinder ID surface

20/300

Fe105W

61

2

6

1.9

Bal

 

15

1

2.5

W:4.50

Centrifugal casting on cylinder ID surface

20/300

Fe105W-1

61

1.5

8

2

Bal

1.3

8

1

3

 

Centrifugal casting on cylinder ID surface

20/300

Fe105W-JC

60

1.5

8

2

Bal

 

8.5

1

3

W:3.20

Centrifugal casting on cylinder ID surface

20/300

FJ-6

57

0.2

13.5

1.5

Bal

2.5

1.1

 

 

 

Centrifugal casting on cylinder ID surface

150/300

FJ-19

60

2.9

30

2

Bal

3

5

 

2.3

 

Centrifugal casting on cylinder ID surface

100/270

FJ-20

64

5

25

 

Bal

 

 

 

1.5

 

Centrifugal casting on cylinder ID surface

100/270


Introduction of Iron alloy powder:
Iron-based powder metallurgy formula technology can also be used in processing the special performance of powder metallurgy products so as to meet different operating requirements of them. In the powder metallurgy formula technology, vibration-assisting filling method is used so as to change the distribution of powder density, thus the powder will be evenly distributed and avoid that the metal powders are not fully and evenly filled, moreover, it also can reduce the crack and failure of powder metallurgy products caused by high frequency induction heating and quenching as it can reduce the induction heating equipment frequency and heating rate as well as lessen the hardness difference between the heating and non-heating area, in which the harness buffer will be generated and reduce crack risks.

 

Centrifugal casting process advantages:

image001.jpg

1.Using centrifugal casting, there will be no fear of length, thickness and diameter. Castings of any length, any thickness and any diameter can be produced and manufactured easily without any limitations. (15 m )
2.Pipes, Fly Wheels and all cylinder liners can be produced using Centrifugal Casting.
3.Different thicknesses of the walls can be manufactured easily.
4.It also eliminates the necessity of the cores.
5.Centrifugal casting has its Mechanical properties at the top.
6.Cylindrical shapes of any size can be produced with ease.
7.Better surface finish can be achieved.
8.Very huge parts of heavy weight can also be produced up to 61,235 kg.